[May1234]

I thought that nobody would write back to me, thank you very much, the product is starting to be stable, the only problem I still have is in the pigments of interference , as I increase the viscosity, it gets mud , but I think I will work it out now, I have to adjust the oils , thank you very much and help

[May1234]

Of course , it is normal….. but I think that you can’t give as much as you want, you can give e.g. 3-6%  if you have not pearl pigment but please remember to be well grated e.g. in castor oil.Titanium white rubbing is very important ,

it is best if you put all the dyes together and chew them together.

[May1234]

Can you send your formulation? We need to  have more information , we don’t know what you used, maybe it is enough to reduce the amount of one light emollient for e.g. larger amounts of castor oil…… but there can be many reasons……….

[May1234]

May1234 said:

Hello.I’m new here.I want to do pressed shadows with very very shiny-unique effect.I have benchnark,Inci name, I did a lot off test and I don’t know where is the problem :

After pressing ,the shadow is brittle,behaves like a pillow but benchamrk is a good tied.i suppose the main ingredients it:

Calcium Sodium Borosilicate (20-100pm)

Synthetics fluorogophite ( interference mika synthetics or white synthetic fluorogophite)

Silica- I’m not sure what kind off Sillica-it’s maybe silica microsphere or silica silica like Aerosil or Wacker HDK15.

Gransil clear gel from Company Grant Inc (inci:Dimethicone and Cyclopentasiloxane and Polysilicone-11)

Pentaerithrityl Tetraisostearate (Crodamol PTIS from CRODA)

Isostearyl Isostearate-Crodmol ISIS from Company Croda

Inci name benchmark:Calcium Sodium Borosilicate,Synthetic Fluorogophite,Silica,Mica,Dimethicone,Cyclopentasiloxane,Polysilicone-11,Pentaerythrityl Tetraisostearate,Isostearyl Isostearate,Phenoxyethanol,Ethylhexylglycerin,{+/_CI77981,77491,77492,77499,77266,77510,77288,45380,19140,15850,15880,77007,77492,45410,TIN OXIDE.

Benchamrk has many colors but I’m sure that this inci is collective formulation.

Could someone help me develop this formulation?

Thanks in advance

Regards

May……

I am straightening my request and inquiry.

It is my formulation:

Calcium Aluminium Borosilicate  Intereference colour (20-100 pm) x
58.41 %

Silica Wacker HDK N20 X 3.095 %

Mika Natural 5.841 %

Pentaerithrytyl Tetraisostearate x 3.95 %

Isostearyl Isostearate - 3.95 %

Gransil clear gel ( Dimethicone&Cyclopentasiloxane & Polysilicone
11) x 24.76 %

Plus preservative about 0.8 % but I didn’t give it to the test trial

The final product is very fluffy, too little gloss, it crumbles.

Can I count on any help, suggestions?

Thank you in advance and best regards to everyone

 

[May1234]

I am straightening my request and inquiry.

It is my formulation:

Calcium Aluminium Borosilicate  Intereference colour (20-100 pm) x 58.41 %

Silica Wacker HDK N20 X 3.095 %

Mika Natural 5.841 %

Pentaerithrytyl Tetraisostearate x 3.95 %

Isostearyl Isostearate - 3.95 %

Gransil clear gel ( Dimethicone&Cyclopentasiloxane & Polysilicone 11) x 24.76 %

Plus preservative about 0.8 % but I didn’t give it to the test trial

The final product is very fluffy, too little gloss, it crumbles.

Can I count on any help, suggestions?

Thank you in advance and best regards to everyone