PRESSED SHADOW WITH CALCIUM ALUM.BOROSILICATE-PROBLEM
Hello.I’m new here.I want to do pressed shadows with very very shiny-unique effect.I have benchnark,Inci name, I did a lot off test and I don’t know where is the problem :After pressing ,the shadow is brittle,behaves like a pillow but benchamrk is a good tied.i suppose the main ingredients it:Calcium Sodium Borosilicate (20-100pm)Synthetics fluorogophite ( interference mika synthetics or white synthetic fluorogophite)Silica- I’m not sure what kind off Sillica-it’s maybe silica microsphere or silica silica like Aerosil or Wacker HDK15.Gransil clear gel from Company Grant Inc (inci:Dimethicone and Cyclopentasiloxane and Polysilicone-11)Pentaerithrityl Tetraisostearate (Crodamol PTIS from CRODA)Isostearyl Isostearate-Crodmol ISIS from Company CrodaInci name benchmark:Calcium Sodium Borosilicate,Synthetic Fluorogophite,Silica,Mica,Dimethicone,Cyclopentasiloxane,Polysilicone-11,Pentaerythrityl Tetraisostearate,Isostearyl Isostearate,Phenoxyethanol,Ethylhexylglycerin,{+/_CI77981,77491,77492,77499,77266,77510,77288,45380,19140,15850,15880,77007,77492,45410,TIN OXIDE.Benchamrk has many colors but I’m sure that this inci is collective formulation.Could someone help me develop this formulation?Thanks in advanceRegardsMay…… -
4 Replies
-
I am straightening my request and inquiry.It is my formulation:Calcium Aluminium Borosilicate Intereference colour (20-100 pm) x 58.41 %Silica Wacker HDK N20 X 3.095 %Mika Natural 5.841 %Pentaerithrytyl Tetraisostearate x 3.95 %Isostearyl Isostearate - 3.95 %Gransil clear gel ( Dimethicone&Cyclopentasiloxane & Polysilicone 11) x 24.76 %Plus preservative about 0.8 % but I didn’t give it to the test trialThe final product is very fluffy, too little gloss, it crumbles.Can I count on any help, suggestions?Thank you in advance and best regards to everyone -
May1234 said:Hello.I’m new here.I want to do pressed shadows with very very shiny-unique effect.I have benchnark,Inci name, I did a lot off test and I don’t know where is the problem :After pressing ,the shadow is brittle,behaves like a pillow but benchamrk is a good tied.i suppose the main ingredients it:Calcium Sodium Borosilicate (20-100pm)Synthetics fluorogophite ( interference mika synthetics or white synthetic fluorogophite)Silica- I’m not sure what kind off Sillica-it’s maybe silica microsphere or silica silica like Aerosil or Wacker HDK15.Gransil clear gel from Company Grant Inc (inci:Dimethicone and Cyclopentasiloxane and Polysilicone-11)Pentaerithrityl Tetraisostearate (Crodamol PTIS from CRODA)Isostearyl Isostearate-Crodmol ISIS from Company CrodaInci name benchmark:Calcium Sodium Borosilicate,Synthetic Fluorogophite,Silica,Mica,Dimethicone,Cyclopentasiloxane,Polysilicone-11,Pentaerythrityl Tetraisostearate,Isostearyl Isostearate,Phenoxyethanol,Ethylhexylglycerin,{+/_CI77981,77491,77492,77499,77266,77510,77288,45380,19140,15850,15880,77007,77492,45410,TIN OXIDE.Benchamrk has many colors but I’m sure that this inci is collective formulation.Could someone help me develop this formulation?Thanks in advanceRegardsMay……
I am straightening my request and inquiry.
It is my formulation:
Calcium Aluminium Borosilicate Intereference colour (20-100 pm) x
58.41 %Silica Wacker HDK N20 X 3.095 %
Mika Natural 5.841 %
Pentaerithrytyl Tetraisostearate x 3.95 %
Isostearyl Isostearate - 3.95 %
Gransil clear gel ( Dimethicone&Cyclopentasiloxane & Polysilicone
11) x 24.76 %Plus preservative about 0.8 % but I didn’t give it to the test trial
The final product is very fluffy, too little gloss, it crumbles.
Can I count on any help, suggestions?
Thank you in advance and best regards to everyone
-
You could add styrene/isoprene crosspolymer or a similar polymer. A clear, high gloss wax could help. Finally, what about stickier oils like hydrogenated polyisobutene?
-
I thought that nobody would write back to me, thank you very much, the product is starting to be stable, the only problem I still have is in the pigments of interference , as I increase the viscosity, it gets mud , but I think I will work it out now, I have to adjust the oils , thank you very much and help
Log in to reply.