@Perry I’d certainly watch!
-
@Belassi Ah yes, thats not a problem, thank you!
@EVchem I’ve tried varying quantities of petro right up to 95% and it just wasn’t the same. It was way too greasy at those amounts and didn’t the elasticity. I think I’ll try different cool down methods and see what happens. Although I am starting to think it is possible that the microcrystalline wax I am using could be contributing to the problem. I think I may need to use a softer grade.
@chemicalmatt I’ll give that a go, thank you very much!
-
@Belassi Thank you for your comment. That is something I noticed and was suspecting it could be my processing.
Do you have any suggestions on processing techniques to help achieve this or know somewhere that I could find this info? Thanks again.